Elasticity and material anisotropy of lamellar cortical bone in adult bovine tibia characterized via AFM nanoindentation.

Abstract

The research focuses on the evaluation of the mechanical properties of osteonal cortical bone at the lamellar level. Elastic properties of the mid-diaphysis region of the bovine tibia are investigated via cantilever-based nanoindentation at the submicron length scale utilizing Atomic Force Microscopy, where the force-displacement curves are used for the elastic assessment using the Derjaguin-Muller-Toropov model to calculate indentation modulus. Variations of the modulus and the directional mechanical response of the osteonal bone at different distances from the Haversian canal are investigated. Additionally, the effects of demineralization on the indentation modulus are discussed. It was found that in the axial direction, the first and last untreated thick lamella layers show a significant indentation modulus difference compared to all other layers (4.26 ± 0.4 and 4.6 ± 0.3 GPa vs ∼3.5 GPa). On the other hand, the indentation modulus of transverse thick lamella layers shows a periodic variation between ∼3 ± 0.7 GPa and ∼4 ± 0.3 GPa from near the Haversian canal to near the interstitial bone. A periodic variation in the anisotropy ratio was found. Mineral content was quantified via energy-dispersive X-ray microanalysis at different levels of mineralization and shows a positive correlation with the indentation modulus.