Form II to form I transition in solution-crystallized isotactic polybutene-1.

Abstract

Different polymer chains in a solution or melt have different conformations with corresponding entropy at each moment, which would be confined after crystallization. Equilibrium concept-based conformation or conformational entropy depends on chain dynamics, which is related to the effect of energy on conformational changes in polymer chains. Herein, an isotactic polybutene-1 (iPB-1) crystal was crystallized from solution by adding a precipitant at various temperatures. The solution-crystallized iPB-1 crystal was heated to 100 °C to obtain form II at different heat rates and the transition of form II was characterized. It was found that the form II to form I transition was not only related to the precipitation temperature but also to the heating rate of the solution-crystallized iPB-1. Thus, both precipitation temperature and heating rate determine the formation temperature of form II, <i>i.e.</i>, form II that crystallized at lower temperature would transform faster. The results indicate that the conformation or conformational entropy of the amorphous region in iPB-1 is important to understand crystal transition.