Colloidal Synthesis and Analysis of CNT-Cu<sub>2</sub>S for Stability and Capacity Increase Alleviation in Sodium-Ion Storage.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 39405386.
- Also identified by DOI 10.1021/acs.nanolett.4c02858 and PMC identifier 11566108.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
With the growing interest in energy storage, significant research has focused on finding suitable anode materials for sodium-ion batteries (SIBs). While developing high-capacity nanosized metal sulfides, issues like low stability and rapid initial capacity decline are common. Instead of maintaining steady capacity, they also tend to exhibit an increase in discharge capacity as cycling continues. We introduce CNT-Cu<sub>2</sub>S, featuring Cu<sub>2</sub>S nanoplates integrated onto the surface of MWCNTs, and assess its electrochemical properties for SIBs. Cu<sub>2</sub>S initially exhibited a rapid decrease in capacity and then showed increased capacity. In contrast, CNT-Cu<sub>2</sub>S demonstrated a stable capacity of 344.8 mAh g<sup>-1</sup> at 2.0 A g<sup>-1</sup> over 800 cycles, close to the theoretical capacity with capacitive behavior. This paper carried out analysis using data from in situ EIS and overpotential data from GITT to explain the different outcomes between the Cu<sub>2</sub>S and CNT-Cu<sub>2</sub>S experiments. These results show that CNT-Cu<sub>2</sub>S is a suitable anode material for SIBs.