Constructing the Enamel-Like Dentin Adhesion Interface to Achieve Durable Resin-Dentin Adhesion.

Abstract

Enamel adhesion is acknowledged as durable; however, achieving long-lasting dentin adhesion remains a formidable challenge due to degradation of exposed collagen matrix after acid-etching of dentin. The idea of developing an enamel-like adhesion interface holds great promise in achieving enduring dentin adhesion. In this study, we constructed an enamel-like adhesion interface using a rapid remineralization strategy comprising an acidic primer and a rapid remineralization medium. Specifically, the acidic primer of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) and epigallocatechin-3-gallate (EGCG) nanocomplex (MDP@EGCG primer) was utilized to partially demineralize dentin within 30 s, and the MDP@EGCG nanocomplex showed a strong interaction with exposed collagen, enhancing collagen remineralization properties. Then, the rapid remineralization medium containing polyaspartate (Pasp) stabilized amorphous calcium and phosphorus nanoclusters (rapid Pasp-CaP) was applied to modified dentin collagen for 1 min, which caused rapid collagen remineralization within a clinically acceptable time frame. This strategy successfully generated an inorganic rough and porous adhesive interface resembling etched enamel, fundamentally addressed issues of collagen exposure, and achieved durable dentin adhesion <i>in vitro</i> and <i>in vivo</i> while also ensuring user-friendliness. It exhibited potential in prolonging the lifespan of adhesive restorations in clinical settings. In addition, it holds significant promise in the fields of caries and dentin sensitivity treatment and collagen-based tissue engineering scaffolds.