The influence of plasticizer on the mechanical, structural, thermal and strain recovery properties following stress-relaxation process of silk fibroin/sodium alginate biocomposites for biomedical applications.

Abstract

The influence of plasticizer glycerol (GLY) on the mechanical, structural, and thermal properties of silk fibroin (SF)/sodium alginate (SA) biocomposite films was investigated in detail. As the SF/SA ratio increased up to 65%, the SF content significantly improved the Tensile strength (σ_T), Young's modulus (E_y) but reduced the elongation at break (ε_b). To modify and enhance the elasticity and flexibility of the biocomposite films, the GLY as a plasticizer was used at different ratio from 20 to 50% for each SF/SA biocomposite films. Although the extensibility of the films was improved greatly with increasing GLY ratio, σ_T and E_y reduced significantly. The effect was observed more apparently for the GLY ratio starting from 35%. It was also shown that crystallinity index in the Amide I region increased as the SF/SA ratio increased to 65%. Increasing SF content improved the thermal stability of the SF/SA biocomposites. The XRD results showed that crystallinity was increased as SF/SA ratio increased. Stress-relaxation of SF/SA (30%) biocomposite films plasticized with GLY revealed that each kind of plasticized films showed a viscoelastic behavior and a fast relaxation in the first stage (1-2 min) of the processes and then continued slowly. The GLY increased the extensibility and elasticity limit of the SF/SA (30%) composite films. During the strain recovery processes, the plasticized composite films recovered completely in a quite shorter time than that of unplasticized films. It was observed higher the GLY content, the recovery times became shorter.