Formation Cycle Control for Enhanced Structural Stability of Ni-Rich LiNi<sub><i>x</i></sub>Co<sub><i>y</i></sub>Mn<sub>1-x-y</sub>O<sub>2</sub> Cathodes.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 39786716.
- Also identified by DOI 10.1021/acsnano.4c10476.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Nickel-rich NCM cathode materials promise lithium-ion batteries with a high energy density. However, an increased Ni fraction in the cathode leads to complex phase transformations with electrode-electrolyte side reactions, which cause rapid capacity fading. Here, we show that an initial formation cycle at 0.1 C with a higher cutoff voltage (≥4.35 V) increases the stability of Ni-rich NCM (LiNi<sub>0.88</sub>Co<sub>0.08</sub>Mn<sub>0.04</sub>O<sub>2</sub>) particles during cycling at 1 C. We unveil that the formation of intragranular nanovoids is directly associated with the initial formation cycle at a lower charging cutoff voltage when oxygen vacancies are introduced at the Ni-rich NCM particle surface, due to irreversible electrolyte decomposition at the cathode-electrolyte interface. Nanovoid evolution of the Ni-rich NCM particles after 50 cycles increases the NiO-like rock salt phase; it results in intragranular cracks, which cause structural instability via heterogeneous phase distribution. This work demonstrates the importance of controlling Ni-rich NCM surface chemistry from the initial formation cycle to achieve better cycling stability.