Formation and Variation of the Superstructure of Cation Ordering in Layered Cathode Materials.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 39960862.
- Also identified by DOI 10.1021/acs.nanolett.4c06598.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
This study employs aberration-corrected transmission electron microscopy to provide definitive evidence of cation ordering within the superstructure of LiNi<sub>0.5</sub>Co<sub>0.2</sub>Mn<sub>0.3</sub>O<sub>2</sub> (NCM523), a prominent Ni-rich ternary cathode material, characterized by wave vector <b><i>q</i></b> = 1/3(2<b>a</b>* - <b><i>b</i></b>*). We show that this ordering can be enhanced through controlled heating. Comparative analysis of LiNi<sub><i>x</i></sub>Co<sub><i>y</i></sub>Mn<sub><i>z</i></sub>O<sub>2</sub> samples with different compositions revealed that Mn ions are crucial for superstructure formation. The battery performance test shows that the superstructure has no obvious effect on the voltage platform during the charge-discharge cycle, but has a negative effect on the cycle performance and structural stability. This study elucidates the origin and detrimental effects of superstructures, advancing the understanding of their impact on battery performance, which is vital for the future development of ternary cathode materials.