Precisely Tuning 3D/Quasi-2D Perovskite Heterojunctions in Wide-Bandgap Perovskites for High-Performance Tandem Solar Cells.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 40488942.
- Also identified by DOI 10.1002/adma.202504321.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Wide-bandgap (WBG) perovskite sub-cells in all-perovskite tandem solar cells (AP-TSCs) suffer from severe open-circuit voltage loss and poor light stability. The formation of 3D/2D or 3D/quasi-2D perovskite heterojunctions can effectively passivate interface defects and optimize energy level alignments at the 3D perovskite/C<sub>60</sub> interface, thereby enhancing both the efficiency and stability of perovskite solar cells. Herein, a combined evaporation/solution technique is employed to construct Dion-Jacobson (DJ) 2D or quasi-2D perovskites with uniform-phase distribution on wide-bandgap 3D perovskite substrates. By tuning the n values of the DJ phase perovskites, well-refined WBG 3D/2D or quasi-2D perovskite heterostructures are achieved, which exhibit tunable energy levels and mitigate the non-radiative recombination losses at the WBG 3D perovskite/C<sub>60</sub> interface. The devices with the WBG (1.78 eV) 3D/quasi-2D n = 3 perovskite heterostructures achieve the champion power conversion efficiency (PCE) of 20.71% (certified 20.53%). When combined with narrow-bandgap (NBG) perovskite sub-cells, the fabricated 2-terminal AP-TSCs achieve a PCE of 28.99% (certified 28.81%). The tandem device maintains 80% of its initial PCE after 501 h of operation at maximum power point.