Nanoscale Engineering of Ladder-Like Polysilsesquioxane Dielectric Surfaces Enables High-Performance Flexible Electronics.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 40658877.
- Also identified by DOI 10.1021/acs.nanolett.5c02268.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Achieving high-performance flexible organic thin-film transistors (OTFTs) operating at low voltages is vital for next-generation electronics. Here, we report a novel ladder-like polysilsesquioxane (LPSQ) dielectric with nanoscale functionalities (long alkyl chains and epoxy groups) that simultaneously enhance organic semiconductor (OSC) self-assembly and dielectric performance. Alkyl chains promote chain-on crystallization of C10-DNTT, while epoxy groups boost dielectric polarization and enable UV photopatterning. This yields an ultralow interface trap density of 6.00 × 10<sup>11</sup> cm<sup>-2</sup> and record-high hole mobility of 15.55 cm<sup>2</sup>/V·s at 5 V. The resulting OTFTs show excellent stability (threshold shift < 1 V over 200 min) and robust flexibility on PET substrates. Moreover, leveraging the dielectric's patternability, fully solution-processed flexible logic circuits (inverters and NAND/NOR gates) with voltage gains of up to 37.2 at 5 V are demonstrated. This work provides a molecular design strategy for high-k LPSQ dielectrics toward practical low-voltage flexible electronics.