Surface-Modified Graphite Anodes for High-Rate Long-Cycling in Sulfide All-Solid-State Batteries.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 40865973.
- Also identified by DOI 10.1021/acsnano.5c05650.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Graphite is a promising anode for realizing high power density in sulfide-based all-solid-state lithium batteries (ASSLIBs). However, their fast-charging capabilities are limited in practice. This paper demonstrates that the reactivity between lithiated graphite and sulfide electrolytes and undesirable side reactions at the amorphous carbon interface negatively affect the fast-charging capacities of ASSLIBs. On this basis, a lithium niobate-coated spherized natural graphite composite (LNO@SNG) synthesized via a scalable sol-gel method was employed to form an electrochemically stable interface with Li<sub>6</sub>PS<sub>5</sub>Cl electrolyte. Full cells assembled with a LiNi<sub>0.7</sub>Co<sub>0.2</sub>Mn<sub>0.1</sub>O<sub>2</sub> cathode and LNO@SNG anode demonstrated cycling stability under low stack pressures (≤5 MPa), at high rates (up to 12C), and even with high cathode loading (30.57 mg·cm<sup>-2</sup>), respectively, and achieved a capacity retention of 96.5% after 600 cycles at 4 mA·cm<sup>-2</sup> (6C). The surface-modified graphite anode combines cost effectiveness, interfacial stability, and superior rate capability, promising to be a major boost for ASSLIB commercialization.