Spatially resolved nanostructural analysis of disordered phases in carbonated alkali-activated slag.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 41381445.
- Also identified by DOI 10.1038/s41467-025-67179-5 and PMC identifier 12804976.
- Licence recorded as CC BY-NC-ND.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Alkali-activated slag (AAS) is a promising low-CO<sub>2</sub> alternative cement consisting of several disordered phases of similar composition. Although their local atomic arrangements are known to influence macroscopic behavior, determination of structural changes in response to external stimuli remains a challenge. Here, X-ray diffraction-computed tomography (XRD-CT), pair distribution function-CT (PDF-CT), and nanoprobe X-ray fluorescence (nano-XRF) have been used to uncover how an increase of magnesium in AAS affects the atomic structure and spatial arrangement of phases after aggressive carbonation (100% dry CO<sub>2</sub>), conditions experienced in applications such as oil and gas wells and geological storage of CO<sub>2</sub>. From PDF-CT it is found that a higher magnesium content decreases the average nanoscale crystallite size of disordered calcium carbonate. At the same time, higher magnesium content is correlated with a less decalcified C-(N)-A-S-H gel, as determined via analysis of Ca-Si atom-atom correlations from PDF-CT and Ca/Si ratios from nano-XRF. Finally, nano-XRF reveals that the disordered (i.e., amorphous) calcium carbonate is stabilized by the presence of silicates.