Impact of Anode to Cathode Crossover in Lithium-metal Batteries With High-Nickel Cathodes.

Abstract

The advancement of high-energy-density lithium-metal batteries (LMBs) is hindered by the chemical instability of both lithium-metal anode and high-nickel layered oxide cathodes. While cathode-to-anode crossover is well-documented, the reverse process of anode-to-cathode crossover remains underexplored. Here, we systematically investigate such crossovers and the degradation pathway in pouch cells with a localized high-concentration electrolyte, comparing NMC622, NMC811, and NMC90 cathodes paired with lithium-metal and graphite anodes. Despite delivering higher initial capacities, LMBs exhibit faster capacity fade under long-term cycling at 45 °C. To isolate cathode-side degradation, galvanostatic electrochemical impedance spectroscopy (GEIS) measurements of cycled cathodes paired with delithiated lithium iron phosphate (LFP) counter electrodes reveal significantly higher charge-transfer resistance in cathodes cycled with lithium-metal. Surface characterization via X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) reveals greater electrolyte decomposition on cathodes cycled with lithium metal, leading to thicker, more organic-rich cathode-electrolyte interphases (CEIs), consistent with the elevated charge-transfer resistance observed in GEIS measurements. Notably, NMC90 shows the most pronounced CEI thickening, linking higher cathode surface reactivity to greater susceptibility to anode-to-cathode crossover. This work presents compelling evidence of crosstalk degradation originating from lithium-metal anodes and underscores the importance of cross-interface stability for the design of durable LMBs.