Modulation of Conductive Filaments in Ag/Cu<sub>2</sub>S/SiO<sub>2</sub>/W Memristor.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 41572509.
- Also identified by DOI 10.1021/acs.nanolett.5c05265.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
For the active-metal/insulator/metal memristor, the reversible formation and annihilation of metallic filaments critically influence the performance. However, efficient methods of controlling filament nucleation sites and growth dimensions remain elusive, particularly for amorphous oxides. In this work, an ionic conductive Cu<sub>2</sub>S layer is introduced to the Ag/SiO<sub>2</sub>/W memristor to restrict the formation pathways of metallic filaments. Localized Cu<sub>2</sub>S phase transition (from the monoclinic phase to the hexagonal phase) and columnar grain boundaries are identified as preferred nucleation and growth sites during SET. This approach suppresses random filament growth within the amorphous SiO<sub>2</sub> layer, overcomes the challenge of high-resistance state recovery, and significantly improves the controllability of filament formation and annihilation. As a result, the Ag/Cu<sub>2</sub>S/SiO<sub>2</sub>/W memristor demonstrates a stable cycling endurance and a switching ratio of up to 10<sup>6</sup>. This work provides experimental insight into controlling the formation of conductive filaments for high-performance memristors.