Perovskite solar cells with enhanced thermal fatigue resistance under extreme temperature cycling.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 41803152.
- Also identified by DOI 10.1038/s41467-026-70293-7 and PMC identifier 13100044.
- Licence recorded as CC BY.
- The licence permits redistribution, so the abstract is shown in full and the full text is available from the publisher.
Abstract
Metal halide perovskite solar cells combine high power density with low-cost manufacturing, but durability under repeated extreme temperature cycling remains insufficiently understood. We investigate thermal fatigue under cycling between -80 °C and +80 °C as an accelerated stress protocol. Mismatched thermal expansion between the perovskite absorber and glass substrate induces biaxial tensile strain, leading to degradation at the substrate-perovskite interface and within grain boundaries. To mitigate these failure modes, we introduce a co-additive molecular strategy based on lipoic acid, dihydrolipoic acid, and a sulfonium-based derivative to enhance interfacial adhesion, while in situ polymerization during annealing reinforces grain-boundary cohesion. This dual reinforcement improves robustness and performance, achieving stabilized efficiencies of 26% under standard solar illumination. Devices retain 84% of initial efficiency after 16 extreme temperature cycles. Our experiments reveal that thermal exposure duration is more critical than cycle number, with most degradation occurring during initial cycles.