Tough asymmetric thermochromic ionogels via dynamic in situ phase separation for dual-modal smart optical switching.
biomechanical · Level V
Where this comes from
- Record sourced from PubMed, PMID 41844627.
- Also identified by DOI 10.1038/s41467-026-70830-4.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Despite significant advances in thermochromic materials (TCMs) for smart optical switching, achieving simultaneous optimization of optical switching, mechanical robustness, and environmental tolerance remains a critical challenge for their real-world implementation. Herein, we present tough asymmetric thermochromic ionogels (ATIs) fabricated via dynamic in situ phase separation. The ATIs integrate a thermoresponsive light-scattering layer (LCST: 28 °C to 41 °C) and a mechanically reinforced supporting layer through sequential free-radical polymerization. The resulting material exhibits high transparency (>85% at 20 °C), ultralow-temperature resistance (transparent at -70 °C, even at -196 °C), and exceptional toughness (tensile strength >5 MPa, toughness >17 MJ m<sup>-3</sup>). Leveraging hydrophobic ionic liquid as solvent, the ATIs achieve reversible optical switching (transmittance <10% at 40 °C) without encapsulation, with autonomous adhesion (>400 N m<sup>-1</sup> peel strength on glass). Applied to smart cooling windows, ATIs reduce solar radiation by 56.8% while enabling aesthetic customization. Combined with indirect/direct Joule heating technology, ATIs enable active optical switching and even dynamic projection display, offering a scalable platform for all-weather adaptive optical systems.