Dipole Reorientation Induced Temperature-Dependent Solvation Structure in Low-Temperature Sodium Metal Batteries.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 41891685.
- Also identified by DOI 10.1021/acsnano.5c21977.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Sodium metal batteries (SMBs) are promising candidates for next-generation energy storage systems due to their high energy density and abundant sodium resources. However, their application is hindered by sluggish interfacial kinetics at low temperatures. We designed a temperature-dependent electrolyte by balancing ion-dipole and dipole-dipole interactions. The electron-withdrawing effect of fluorine (F) atoms increases the instability of the fluoroethylene carbonate (FEC) dipole orientation within the solvation shell. As temperature decreases, FEC's dipole reorientation triggers a shift from an ethyl methyl carbonate (EMC)-dominated solvation structure to an FEC-dominated one. This significantly reduces the desolvation energy of solvent-separated ion pairs (SSIPs), contact ion pairs (CIPs), and aggregates (AGGs), accelerating interfacial kinetics. It also reorganizes the solvation structure and alters the decomposition pathway of the electrolyte, forming a thin, organic-rich CEI layer at low temperatures. As a result, P2-Na<sub>2/3</sub>Ni<sub>1/3</sub>Mn<sub>2/3</sub>O<sub>2</sub> (P2-NNMO) and O3-NaNi<sub>1/3</sub>Fe<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub> (O3-NFM) cells demonstrate reliable performance, achieving a high-capacity retention of 92.4% after 1000 (1 C) and 84.7% after 900 (0.5 C) cycles at -20 °C. Notably, the P2-NNMO and O3-NFM cells deliver reversible discharge capacities of 80.6 and 102.3 mAh g<sup>-1</sup> at -40 °C, respectively. This work offers valuable insight for advancing energy storage technologies.