Adsorption-Engineered Hydrocarbon Ionomers for Durable Proton-Exchange Membrane Fuel Cells.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 42581713.
- Also identified by DOI 10.1002/adma.74561.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Reducing reliance on perfluoroalkyl substances (PFAS) in proton-exchange membrane fuel cells requires hydrocarbon ionomers that combine high performance with long-term durability, a persistent challenge in catalyst-layer design. Here, we identify oxidation-driven ionomer-catalyst interfacial degradation as a dominant failure pathway in hydrocarbon ionomer-bonded cathodes and introduce an adsorption-engineering strategy to overcome this limitation. The comparison of a commercial sulfonated poly(phenylene) (Pemion) with structurally engineered sulfonated poly(fluorene)s demonstrated that electrode durability is governed by the interplay between ionomer adsorption strength and resistance to oxidative degradation on carbon-supported Pt catalysts. A poly(fluorene) ionomer with mobile alkyl sulfonic acid groups forms resilient interfaces, delivering 1.28 A cm<sup>-</sup> <sup>2</sup> at 0.65 V under fully humidified H<sub>2</sub>/air conditions (80°C and 150 kPa<sub>abs</sub>), comparable to Pemion. After 90,000 accelerated potential cycles, the poly(fluorene)-bonded cathode exhibits significantly improved durability, with only 29% performance loss compared to 58% for Pemion; further molecular refinement reduces the loss to 17%, approaching that of Nafion-bonded cathodes (14%). These findings establish adsorption-engineered ionomer design that decouples interfacial anchoring from oxidative degradation as a general strategy for achieving durable, high-performance PFAS-free PEM fuel cell electrodes.