Preliminary study of the effect of aging following irradiation on the wear of ultrahigh-molecular-weight polyethylene.

Abstract

Several studies have indicated that degradation of ultrahigh-molecular-weight polyethylene following gamma irradiation in air adversely affects the mechanical properties of the material; however, it is not known how this subsequently affects its wear rate. Wear studies have therefore been performed on three groups of ultrahigh-molecular-weight polyethylene; unirradiated material, recently irradiated material (aged for 2 months), and aged irradiated material (aged for 5 years). The aging took place in sterile packaging on the shelf. The wear studies were carried out on a tri-pin-on-disk wear tester, with a pin from each type of material being studied in each test. In each test the wear rate of the nonirradiated material was slightly lower than the 2-month-aged, irradiated material. The 5-year-aged, irradiated material had the highest wear rate, and this was significantly greater than that of the unirradiated material (P < .05).